Petrothene® NA283245
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fbcowo_PetrotheneNA283245.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA283245 is a homopolymer resin that combines clarity with strength and stiffness. In addition, NA283245 exhibits good impact strength on both flat and creased film. NA283245 provides enhanced clarity and sparkle in thin packaging films, such as bread and bakery bags. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D638 | ||
| 1% secant, MD : 25 µm, cast film | 207 | MPa | ASTM D638 |
| 1% secant, TD : 25 µm, cast film | 234 | MPa | ASTM D638 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, extruded film | 8.96 | MPa | ASTM D882 |
| TD : Yield, 25 µm, extruded film | 8.96 | MPa | ASTM D882 |
| MD : Broken, 25 µm, extruded film | 19.3 | MPa | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 13.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, extruded film | 320 | % | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 470 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, cast film | 180 | g | ASTM D1922 |
| TD : 25 µm, cast film | 240 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (45, 25.4 µm, cast film) | 82 | ASTM D523 | |
| Haze (25.4 µm, Cast Film) | 4.8 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPPLEN® R 959 A | MOL Petrochemicals Co. Ltd. | PP Random Copolymer | TIPPLEN® |
| XYLEX™ X7509HP resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |
| 3M™ Dyneon™ PTFE Compound TF 2274 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| LNP™ THERMOCOMP™ RC008ESS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |
| Sylvin 9058-90UV Red 671 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |