DURANEX® 209AW
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | DURANEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fb1f9o_DURANEX-209AW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low Friction, Low Wear, Unfilled, Standard |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 52.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 2780 | MPa | ISO 178 |
| Flexural Stress | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 73.0 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | Internal method | ||
| Flow : 23 to 55°C | 1.0E-4 | cm/cm/°C | Internal method |
| Lateral : 23 to 55°C | 1.0E-4 | cm/cm/°C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Number | EF2001 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Holding Pressure | 60.0 - 100 | MPa | |
| Screw Speed | 100 - 150 | rpm |
| Injection instructions |
|---|
| Cooling Time: Plasticization time + alpha or time without sticking in mold |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RMA 78 | Ronald Mark Associates, Inc. | PVC Homopolymer | RMA |
| Shandong PA1212 A4S11 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| TOTAL Polypropylene PPH 7059 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| NOVAPOL® HB-W355-A | NOVA Chemicals | HDPE | NOVAPOL® |
| Evoprene™ Super G 934 | AlphaGary | SEBS | Evoprene™ Super G |