Nypol® PA B3 D40 NTLA010 NT394
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fag3gk_Nypol-PA-B3-D40-NTLA010-NT394.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Natural Nylon 6 reinforced with 40% aluminum silicate, ideal for injection molding, good set of thermal properties, electrical and mechanical. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.42 to 1.45 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.20 | -- | % | ASTM D955 |
| Ash Content | 38 to 42 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4500 | 2250 | MPa | ASTM D638 |
| Tensile Strength | 250 | 157 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.0 | 9.0 | % | ASTM D638 |
| Flexural Modulus | 17800 | -- | MPa | ASTM D790 |
| Flexural Strength | 78.0 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (Area) | -- | 13.6 | kJ/m² | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | -- | °C | ASTM D648 |
| Melting Temperature | 210 to 225 | -- | °C | ASTM D2117 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 111 G3 | Taro Plast S.p.A. | PET | TAROLOX |
| Iupiace® AH80 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Braskem PE CP 396XP | Braskem | PP Impact Copolymer | Braskem PE |
| Optix® MS-983 | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |
| LEXAN™ EXL9112 resin | SABIC Innovative Plastics | PC | LEXAN™ |