RTP 4082 TFE 10
| Category: | PPA , Polyphthalamide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FZgTuQ_RTP-4082-TFE-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18mm, injection molding | 0.10 - 0.20 | % | ASTM D955 |
| 6.35mm, injection molding | 0.20 - 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.23 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 15200 | MPa | ASTM D638 |
| Tensile Strength | 145 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 1.3 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 11000 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 258 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 430 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Injection Molded) | 254 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammibility, UL 94, was tested in accordance with RTP Company methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 296 - 324 | °C | |
| Middle Temperature | 296 - 324 | °C | |
| Front Temperature | 296 - 324 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Injection Pressure | 69.0 - 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP HLR102 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| XANTAR® G8F 23 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| EMOPLEN® HP MTF 5 | EMAS Plastik San.Tic.AS. | PP Homopolymer | EMOPLEN® |
| Halene H B5500 | Haldia Petrochemicals Ltd. | HDPE, HMW | Halene H |
| HiFill® PBT G/CF30 IM | Techmer Engineered Solutions | PBT | HiFill® |