MAJ'ECO CP464W
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FXndxl_MAJ-ECO-CP464W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO CP464W is a 40% wood fibre reinforced polypropylene compound intended for injection moulding. MAJ'ECO CP464W has been developed especially for demanding applications in various engineering sectors. MAJ'ECO CP464W is UV stabilised. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3200 | MPa | ISO 178 |
| Flexural Stress 2 | 51.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 153 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 114 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 150 - 190 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BJB Polyurethane TC-8750 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| BUP 625 | Bonyan Kala Chemie Company | Polyester, TS | BUP |
| Clyrell EC140R | LyondellBasell Industries | PP, Unspecified | Clyrell |
| Hanwha Total PP BJ820T | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| HiFill® PA6 CM30 L | Techmer Engineered Solutions | Nylon 6 | HiFill® |