TRIREX® Compound 3025GNH15
| Category: | PC , Polycarbonate |
| Manufacturer: | Samyang Corporation |
| Trademark: | TRIREX® Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FXW4Vm_TRIREX-Compound-3025GNH15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRIREX® Compound 3025GNH15 is a Polycarbonate (PC) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 88.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 4410 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 137 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 151 | °C | |
| 1.8 MPa, Unannealed | 146 | °C | |
| CLTE - Flow | 3.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 31 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.11 | ASTM D150 | |
| Dissipation Factor | 9.7E-3 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 MV HI H K1416 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Cheng Yu N6G10 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| Flexirene® MS 40 U | Versalis S.p.A. | LLDPE | Flexirene® |
| Ecobarrier® 0914 | Noble Polymers | Polyolefin, Unspecified | Ecobarrier® |
| LNP™ LUBRICOMP™ RFL33 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |