Hylex® P1010G10HB
| Category: | PC , Polycarbonate |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FXMCwL_Hylex-P1010G10HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate, 10% Glass Filled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.50 | % | ISO 294-4 |
| Water Absorption (24 hr) | 0.14 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 83.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 13 | % | ISO 527-2 |
| Flexural Modulus | 3450 | MPa | ISO 178 |
| Flexural Stress | 124 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 146 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 143 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyopt® LM11 | Suzhou OMAY Optical Materials Co., Ltd | Film, PMMA | Polyopt® |
| Spartech Polycom PP5220 B187 | Spartech Polycom | PP Homopolymer | Spartech |
| Tufel® II 94705 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| Formolene® L63568U | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| Leona™ 14G15 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |