ENFLEX VU-424-55A
| Category: | PP+EPDM , Polypropylene + EPDM Rubber |
| Manufacturer: | Ravago Group |
| Trademark: | ENFLEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FWWrvR_ENFLEX-VU-424-55A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Economical, vulcanized EPDM/PP series |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 55 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% Strain | 1.20 | MPa | |
| 300% Strain | 2.30 | MPa | |
| Tensile Stress (Break) | 5.00 | MPa | ISO 37 |
| Tensile Elongation (Break) | 600 | % | ISO 37 |
| Tear Strength | 28 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 15 | % | |
| 70°C, 22 hr | 36 | % | |
| 100°C, 22 hr | 69 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (125°C, 336 hr) | 1.8 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (125°C, 336 hr) | 610 | % | ISO 188 |
| Change in Shore Hardness in Air (Shore A, 125°C, 336 hr) | -3.0 -3.0 | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -55.0 | °C | ISO 974 |
| Maximum Dynamic Service Temperature | 135 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULATEC® PEEK NV 12 | A. Schulman Europe | PEEK | SCHULATEC® |
| NEXT REGRIND POMC M90-300RG | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REGRIND |
| Axpoly® PP19 1033 | Axion Polymers | PP Homopolymer | Axpoly® |
| Escorene™ Ultra UL 15019CC | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| INEOS Wire & Cable BPD8128 | INEOS Olefins & Polymers Europe | LDPE | INEOS Wire & Cable |