OmniTech™ ABS 30
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniTech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FW3UtG_OmniTech-ABS-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ford Spec# WSB M4D 908A Approved, Heat Resistant ABS |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 4.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 42.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 96.1 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 | °C | |
| Drying Time | < 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 204 to 249 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 216 to 260 | °C | |
| Nozzle Temperature | 216 to 260 | °C | |
| Processing (Melt) Temp | 216 to 260 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAPPO™ J100 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| TOPAS® 6013S-04 | Polyplastics Co., Ltd. | COC | TOPAS® |
| NOVAPOL® GF-0218-F | NOVA Chemicals | LLDPE | NOVAPOL® |
| ECO PELLET® AC55C | UMG ABS, Ltd. | PC+ABS | ECO PELLET® |
| Petrothene® YR19600B | LyondellBasell Industries | Polyolefin, Unspecified | Petrothene® |