TYNE® ABS CBE 75
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Tyne Plastics LLC. |
| Trademark: | TYNE® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FVK2ac_TYNE-ABS-CBE-75.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Data was measured on natural colored test specimens. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 49.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.9 | % | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength | 73.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 104 | °C | |
| 1.8 MPa, Annealed | 102 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ronalen M40 | Roonamid a.s. | PP, Unspecified | Ronalen |
| NYLOY® MC-0030N | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Panlite® AM-1300 | TEIJIN LIMITED | PC Alloy | Panlite® |
| Petrotene® PP A2 T20 PRTA011 PH202 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Sumiliteresin® PR-53074 | SBHPP | Phenolic | Sumiliteresin® |