Plaslube® PPS GF40 TL13
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FVIhue_Plaslube-PPS-GF40-TL13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube® PPS GF40 TL13 is a Polyphenylene Sulfide (PPS) product filled with 40% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 169 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 14100 | MPa | ASTM D790 |
| Flexural Strength | 276 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 282 | °C | |
| 1.8 MPa, Unannealed | 271 | °C | |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 22 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 163 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 288 to 304 | °C | |
| Middle Temperature | 316 to 343 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 316 to 332 | °C | |
| Processing (Melt) Temp | 324 to 338 | °C | |
| Mold Temperature | 129 to 163 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend庐 UT250 | Covestro - Polycarbonates | PC+PET | Makroblend® |
| Thanelene® TPU S80A15 PRTA010 TP305 MSP | Petropol Industry and Trade of Polymers LTDA | TPU-Polyester | Thanelene® TPU |
| ALTECH® PA6 A 1000/107 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| KOCETAL® K300EW | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Hostacom PC072-3 natural | LyondellBasell Industries | PP Homopolymer | Hostacom |