Toyolac® TP88
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FVE9TN_Toyolac-TP88.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® TP88 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 | g/cm³ | ASTM D792 |
| 23°C | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.80 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 96 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 35.0 | MPa | ASTM D638 |
| 23°C | 39.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 10 | % | ASTM D638 |
| Break, 23°C | 17 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1670 | MPa | ASTM D790 |
| 23°C | 1610 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 55.0 | MPa | ASTM D790 |
| 23°C | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 98 | J/m | |
| 23°C, 12.7 mm | 180 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 95.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+12 | ohms | ASTM D257 |
| Electrostatic Voltage 1(23°C) | 1000 | V | Internal Method |
| Half-life of Electrostatic Voltage Decay 2(23°C) | 0.8 | sec | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50%, 24 hr |
| 2 . | 50%, 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PA66 HF230 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 66 | Sunny® |
| Fainplast PVC FK 76 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Lupolen 2420 F | LyondellBasell Industries | LDPE | Lupolen |
| TECHNYL® B 218 V20 BLACK 21N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |
| PONACOM PS 5380 | Ponachem Compound GmbH | PS (HIPS) | PONACOM PS |