HANWHA LLDPE 3120
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FUA0z9_HANWHA-LLDPE-3120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LLDPE 3120 is manufactured by Unipol process and designed for general purpose and agricultural film . LLDPE 3120 has well balanced property of mechanical property, processability and optical property. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 21.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 900 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm | 41.2 | MPa | ASTM D882 |
| TD : Break, 30 µm | 37.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 650 | % | ASTM D882 |
| TD : Break, 30 µm | 750 | % | ASTM D882 |
| Dart Drop Impact (30 µm) | 140 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 30.0 µm | 117.7 | kN/m | ASTM D1004 |
| TD : 30.0 µm | 122.6 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 |
| Peak Melting Temperature | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 10 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.03 to 0.1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT D201 FB52 | Polykemi AB | PBT | POLYshine |
| Siloxane Masterbatch MB50-313 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| TEKAMID™ HG20L | Mando Advanced Materials Co., Ltd. | ABS+Nylon | TEKAMID™ |
| STARFLEX® P 7055 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | STARFLEX® |
| DynaPath™ 267NL | Polymer Dynamix | PE, Unspecified | DynaPath™ |