DOMAMID® A1-026-B20 V10-B
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics GmbH |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FTMMCY_DOMAMID-A1-026-B20-V10-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, 20% glass bead & 10% glass fiber reinforced, black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 55.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 23°C, 72 hr | 1.2 | % | |
| Flow : 23°C, 72 hr | 0.70 | % | |
| Water Absorption 2 | ISO 62 | ||
| Saturation, 23°C | 1.8 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 145 | cm³/g | ISO 307 |
| Ash Content (650°C) | 30 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 115 | MPa | |
| Break | 115 | MPa | |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/20 |
| Flexural Modulus 3 | 4800 | MPa | ISO 178 |
| Flexural Stress 4 | 185 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Melting Temperature | 222 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | VDE 0303-3 |
| Volume Resistivity | 1.0E+15 | ohms·cm | VDE 0303-3 |
| Note Message | |
|---|---|
| 1 . | 50%RH, between 16 to 72 hrs |
| 2 . | 24 hrs |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRILAC AG1000 | Formosa Plastics Corporation | ABS | TAIRILAC |
| Vi-Chem PVC V143-60I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Hypro® PPC-CC20 NATURAL | Entec Polymers | PP Copolymer | Hypro® |
| Karina CLEAR PVC COMPOUND -E 75/316-IS-RG (GLASS CLEAR) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Makrolon® Solid Sheet AR | Covestro - Polycarbonates | PC | Makrolon® Solid Sheet |