RAMSTER PF302G3
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMSTER |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FRW4eC_RAMSTER-PF302G3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% GLASS FIBER REINFORCED, UV STABILIZED PBT FOR INJECTION MOULDING APPLICATION. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 17 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 | % | ASTM D955 |
| -- | 0.40 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.40 | % | ASTM D570 |
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 4400 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 140 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 55 | J/m | ASTM D256 |
| 23°C | 5.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 220 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 225 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 35 34 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.60 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | 650 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 235 - 255 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 245 - 270 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 30.0 - 105 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6944 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TECHNYL® C 216 V35 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Spartech Polycom SCR7F-7010U | Spartech Polycom | PC | Spartech |
| Next PMMA AX-01YW.(MH-3121) | Next Polymers Ltd. | Acrylic (PMMA) | Next PMMA |
| Polimid B 50 GF | Poliblend S.p.a. | Nylon 6 | Polimid B |