AKROMID® A3 GF 33 1 black (2935)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FRQqEY_AKROMID-A3-GF-33-1-black-2935-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 33 1 black (2935) is an 33% glass fibre reinforced , heat stabilised polyamide 6.6 with high stiffness and strength. Applications are mainly components in mechanical engineering and automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Water Absorption (Saturation, 23°C) | 4.7 to 5.3 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.8 to 2.0 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 33 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11500 | 8200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 210 | 140 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 5.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 80 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 220 | -- | °C | ISO 75-2/C |
| Melting Temperature 1 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 10 K/min, DSC |
| 2 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO F-3910 | Prime Polymer Co., Ltd. | PP Random Copolymer | PRIME TPO |
| Unipren® Elastomers A3 NTLA010 90A IM01S1 UP327 | Petropol Industry and Trade of Polymers LTDA | TP, Unspecified | Unipren® Elastomers |
| Elvacite® 2008 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |
| RTP Radel R-7159 | RTP Company | PPSU | RTP |
| Sylvin 9604-90 Grey 9614 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |