RTP 2200 LF AR 15
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FQNgiG_RTP-2200-LF-AR-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aramid Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 - 1.5 | % | ASTM D955 |
| Moisture Content | 0.10 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5520 | MPa | ASTM D638 |
| Tensile Strength | 93.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 - 6.0 | % | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Flexural Strength | 162 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 590 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 3.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 349 - 399 | °C | |
| Mold Temperature | 163 - 218 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® F701-BID-20 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| KOPLA PA6 KNG1020 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| INEOS HDPE T50-1000-178 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| Iupital® FV-30 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| PENTAMID B GV25 H schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |