Maxxam™ FR PP 301 BLK 1284-11 S
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ FR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FQ2CC0_Maxxam-FR-PP-301-BLK-1284-11-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V-0, and 5VA performance ratings. In addition, many compounds in the Maxxam FR portfolio offer elevated Relative Thermal Index (RTI) ratings. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 4.0 to 12 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 28.3 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 230 | % | ASTM D638 |
| Flexural Modulus | 1100 | MPa | ASTM D790 |
| Poisson's Ratio 4 | 0.43 | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 27 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 90.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 41 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.750 mm | PLC 1 | ||
| 1.50 mm | PLC 1 | ||
| 3.00 mm | PLC 1 | ||
| High Voltage Arc Resistance to Ignition (HVAR) | UL 746 | ||
| 0.750 mm | PLC 1 | ||
| 1.50 mm | PLC 1 | ||
| 3.00 mm | PLC 1 | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.750 mm | PLC 4 | ||
| 1.50 mm | PLC 3 | ||
| 3.00 mm | PLC 2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm, (NC and Black) | V-0 | ||
| 1.50 mm, (NC and Black) | V-0 | ||
| 3.00 mm, (NC and Black) | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 775 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Measured on Natural |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-101 | Teknor Apex Company | TPE | Telcar® |
| 4PROP® 9C12420 IUV | 4Plas | PP Copolymer | 4PROP® |
| Adell Polyamide BJ-13 Glass Reinforced Mineral Filled | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| PLASTRON™ PA66-GF50-01 | Daicel Polymer Ltd. | Nylon 66 | PLASTRON™ |
| LNP™ LUBRILOY™ R2000A compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |