SABIC® LDPE HP4023W
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FOoUR2_SABIC-LDPE-HP4023W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description HP4023W is Low Density Polyethylene grade suitable for producing general purpose films and contains slip and antiblock additives. It gives excellent processability and optical properties with good mechanical properties. Typical Applications HP4023W can be used for high clarity laundry bags, textile wrapping films, produce bags, zip lock bags. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 4.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 30 µm, blown film | 60.0 | MPa | ASTM D882 |
| 1% secant, TD : 30 µm, blown film | 170 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 7.00 | MPa | ASTM D882 |
| TD : Yield, 30 µm, blown film | 7.00 | MPa | ASTM D882 |
| MD : Broken, 30 µm, blown film | 18.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 15.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 270 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 540 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 60 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, blown film | 150 | g | ASTM D1922 |
| TD : 30 µm, blown film | 120 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 91.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 75 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured by producing 30 µ film with 2.5 BUR using 100% HP4023W. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 175 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4PROP® 9D02420 FR5HUV | 4Plas | PP Homopolymer | 4PROP® |
| AKROMID® B3 natural (1024) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| apigo® DP 1428 UVR | API SpA | TPO (POE) | apigo® |
| INEOS PP T10G-03 | INEOS Olefins & Polymers USA | TPO | INEOS PP |
| Vipel® K026-PTA-20 | AOC, L.L.C. | Vinyl Ester | Vipel® |