Teflon® PFA 350

Category:	PFA , Perfluoroalkoxy
Manufacturer:	DuPont Fluoropolymers
Trademark:	Teflon® PFA
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	FNctMG_Teflon-PFA-350.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
For inventory control purposes product name may be followed by an X. Products labeled PFA 350 and PFA 350 X are equivalent and all information in this document is applicable to both. Typical Application Applications for DuPont™ Teflon ® PFA 350 include extruded tubing for use in handling aggressive fluids at high pressures; chemical linings for pipes used in the chemical processing industry; film for high flex service; and traditional extruded, injection-molded, or blow-molded articles requiring the unique performance of Teflon ® . Description DuPont™ Teflon ® PFA 350 is a general-purpose fluoroplastic resin available in pellet form. Compared with other grades of Teflon ® PFA, its most unique features are a relatively low flow rate, greatly increased flex life, and enhanced resistance to environmental stress-cracking over both Teflon ® PFA 340 and 345 (Teflon ® PFA 350 has a typical MIT folding endurance of 500,000*, compared to that of 15,000 and 50,000 for Teflon ® PFA 340 and 345 respectively). Teflon ® PFA 350 is preferred when extended service is required in hostile environments involving chemical, thermal, and mechanical stress. Table 1 shows the typical property data for Teflon ® PFA 350. Teflon ® PFA 350 is used when traditional extrusion and molding processes are required for producing products with the superior properties of a fluoroplastic resin. Compared to other thermoplastics, the high melt strength and thermal stability of Teflon ® PFA 350 can be used to improve processing rates. Compared with other fluoroplastics, creep resistance at high service temperatures provides a superior balance and level of end-use properties. Teflon ® PFA 350 combines the processing ease of conventional thermoplastics with many properties similar to those of polytetrafluoroethylene. Properly processed products made from neat Teflon ® PFA 350 resin provide the superior properties characteristic of fluoroplastic resins: chemical inertness, exceptional dielectric properties, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption, low flammability, performance at temperature extremes, and excellent weather resistance. In a flame situation, products of Teflon ® PFA 350 resist ignition and do not promote flame spread. When ignited by flame from other sources, their contribution of heat is very small and added at a slow rate with very little smoke. Teflon ® PFA 350 meets the requirements of ASTM D3307, Type III

Message

For inventory control purposes product name may be followed by an X.

Products labeled PFA 350 and PFA 350 X are equivalent and all information in this document is applicable to both.

Typical Application
Applications for DuPont™ Teflon ® PFA 350 include extruded tubing for use in handling aggressive fluids at high pressures; chemical linings for pipes used in the chemical processing industry; film for high flex service; and traditional extruded, injection-molded, or blow-molded articles requiring the unique performance of Teflon ® .

Description
DuPont™ Teflon ® PFA 350 is a general-purpose fluoroplastic resin available in pellet form. Compared with other grades of Teflon ® PFA, its most unique features are a relatively low flow rate, greatly increased flex life, and enhanced resistance to environmental stress-cracking over both Teflon ® PFA 340 and 345 (Teflon ® PFA 350 has a typical MIT folding endurance of 500,000*, compared to that of 15,000 and 50,000 for Teflon ® PFA 340 and 345 respectively). Teflon ® PFA 350 is preferred when extended service is required in hostile environments involving chemical, thermal, and mechanical stress. Table 1 shows the typical property data for Teflon ® PFA 350.

Teflon ® PFA 350 is used when traditional extrusion and molding processes are required for producing products with the superior properties of a fluoroplastic resin. Compared to other thermoplastics, the high melt strength and thermal stability of Teflon ® PFA 350 can be used to improve processing rates. Compared with other fluoroplastics, creep resistance at high service temperatures provides a superior balance and level of end-use properties. Teflon ® PFA 350 combines the processing ease of conventional thermoplastics with many properties similar to those of polytetrafluoroethylene.

Properly processed products made from neat Teflon ® PFA 350 resin provide the superior properties characteristic of fluoroplastic resins: chemical inertness, exceptional dielectric properties, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption, low flammability, performance at temperature extremes, and excellent weather resistance.

In a flame situation, products of Teflon ® PFA 350 resist ignition and do not promote flame spread. When ignited by flame from other sources, their contribution of heat is very small and added at a slow rate with very little smoke.

Teflon ® PFA 350 meets the requirements of ASTM D3307, Type III

General Information
Features	Low friction coefficient Low hygroscopicity Low smoke High ESCR (Stress Cracking Resistance) Good electrical performance Good creep resistance Good melt strength Good flexibility Low liquidity Good chemical resistance Good weather resistance Heat resistance, medium Thermal stability, good Good toughness
Uses	Films Lining Blow molding applications Pipe fittings
Forms	Particle
Processing Method	Blow molding Extrusion Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.15	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (372°C/5.0 kg)	2.0	g/10 min	ASTM D3307, ISO 12086
Water Absorption (24 hr)	< 0.030	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	55		ASTM D2240, ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D3307, ISO 12086
23°C	28.0	MPa	ASTM D3307, ISO 12086
250°C	14.0	MPa	ASTM D3307, ISO 12086
Tensile Elongation			ASTM D3307, ISO 12086
Fracture, 23°C	300	%	ASTM D3307, ISO 12086
Fracture, 250°C	500	%	ASTM D3307, ISO 12086
Flexural Modulus			ASTM D790, ISO 178
23°C	625	MPa	ASTM D790, ISO 178
250°C	69.0	MPa	ASTM D790, ISO 178

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	305	°C	ASTM D4591

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+18	ohms·cm	ASTM D257, ISO 1325
Dielectric Strength
0.250 mm ¹	80	kV/mm	ASTM D149
0.250 mm	80	kV/mm	IEC 60243-1
Dielectric Constant (1 MHz)	2.03		ASTM D150, IEC 60250
Dissipation Factor (1 MHz)	< 2.0E-4		ASTM D150, IEC 60250

Flammability	Nominal Value	Unit	Test Method
Flame Rating ²	V-0		UL 94
Oxygen Index	> 95	%	ASTM D2863, ISO 4589-2

Additional Information	Nominal Value	Unit	Test Method
Critical Shear Rate (372°C)	12.0	sec^-1
MIT Folding Endurance ³(200.0 µm)	5.0E+5	Cycles	ASTM D2176
Weather and Chemical Resistance: Outstanding

Note Message
1 .	Method A (short time)
2 .	These results are based on laboratory tests under controlled conditions and do not reflect performance under actual fire conditions, current rating is a typical theoretical value.
3 .	Depending on fabrication conditions

Resin Grade	Manufacturer	Category	Trademark
RTP 2100 AR 15 TFE 15	RTP Company	PEI	RTP
Stat-Tech™ AS-10CF/000 Black	PolyOne Corporation	ABS	Stat-Tech™
Borealis PP HA104E	Borealis AG	PP Homopolymer	Borealis PP
LUVOCOM® 1850-9003	LEHVOSS Group	PBT	LUVOCOM®
Sylvin 8600-64D Grey 9456	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin