LNP™ THERMOCOMP™ DX05477 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FMmT2q_LNP-THERMOCOMP-DX05477-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DX05477 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant. Also known as: LNP* THERMOCOMP* Compound DFA-113 EM MR Product reorder name: DX05477 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.59 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2830 | MPa | ASTM D638 |
| -- | 3600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 62.7 | MPa | ASTM D638 |
| Yield | 70.7 | MPa | ISO 527-2 |
| Break | 57.2 | MPa | ASTM D638 |
| Break | 69.4 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.2 | % | ASTM D638 |
| Yield | 3.8 | % | ISO 527-2 |
| Break | 7.4 | % | ASTM D638 |
| Break | 4.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3450 | MPa | ASTM D790 |
| -- | 3700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 120 | MPa | ASTM D790 |
| -- | 121 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 97 | J/m | ASTM D256 |
| 23°C 2 | 7.4 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 5.60 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 145 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 139 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 136 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 333 65A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Celstran® PPS-SF6-01 AF3005 Natural | Celanese Corporation | PPS | Celstran® |
| Globalene® 6181 | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| Kingfa HG-168AI | Kingfa | PP, Unspecified | Kingfa |
| OmniTech™ PBT TF23 PG | OMNI Plastics, LLC | PBT | OmniTech™ |