Leona™ TR161
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FMiqg2_Leona-TR161.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ TR161 is a Polyamide 66 (Nylon 66) product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ TR161 include automotive, electrical/electronic applications, engineering/industrial parts and wire & cable. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.11 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 1.7 to 2.2 | -- | % | Internal Method |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.9 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.9 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | 98 | ASTM D785, ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | 1100 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Yield, 23°C | 72.0 | 46.0 | MPa | ISO 527-2 |
| Break, 23°C | 64.0 | -- | MPa | ISO 527-2 |
| -- | 70.0 | 47.0 | MPa | ASTM D638 |
| Tensile Strain | ||||
| Yield, 23°C | 4.5 | 22 | % | ISO 527-2 |
| Break | 20 | 220 | % | ASTM D638 |
| Break, 23°C | 15 | > 100 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 2500 | 1400 | MPa | ASTM D790 |
| 23°C | 2200 | 1000 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 98.0 | 49.0 | MPa | ASTM D790 |
| 23°C | 88.0 | 38.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 7.00 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 15 kJ/m² | No Break | ISO 179 | |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 | |
| Notched Izod Impact | 170 | 1200 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 225 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 209 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 77.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 66.0 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 7.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 6 B11^ F50 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Starex WR-9310 | SAMSUNG SDI CO., LTD. | ASA | Starex |
| CET® 116 | Resirene, S.A. de C.V. | Acrylic (SMMA) | CET® |
| Eltex® PF6612KJ | INEOS Olefins & Polymers Europe | mLLDPE | Eltex® |
| Leona™ 1300G | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |