PULSE™ 2013
| Category: | PC+ABS , PC/ABS Engineering Resin |
| Manufacturer: | Trinseo |
| Trademark: | PULSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FLaUwo_PULSE-2013.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PULSE 2013 is a talc-filled PC/ABS which provides an optimized balance of properties with low CLTE. This grade is precolored black. Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183/A |
| Apparent Density | 0.74 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.9 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.42 | % | ISO 294-4 |
| Flow direction | 0.35 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4310 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.8 | MPa | ISO 527-2/50 |
| Fracture | 48.9 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.0 | % | ISO 527-2/50 |
| Fracture | 4.7 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3950 | MPa | ISO 178 |
| Flexural Stress 2 | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/A | ||
| -30°C | 5.8 | kJ/m² | ISO 180/A |
| 23°C | 6.2 | kJ/m² | ISO 180/A |
| Instrumented Dart Impact 3 | |||
| -30°C, Peak Energy | 37.2 | J | |
| 23°C, Peak Energy | 32.8 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 124 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 108 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 122 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -30 to 80°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : -30 to 80°C | 5.8E-5 | cm/cm/°C | ISO 11359-2 |
| Additional Information |
|---|
| Tests conducted on 4 mm injection molded specimen, unannealed, unless noted. |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 6.60 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ 7050 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Yuyao PPO GFN3-801 | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| ELASTOSIL® LR 3843/30 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Hyflon® PFA P120X | Solvay Specialty Polymers | PFA | Hyflon® PFA |
| Softell TKG 300N 1 G22843 | LyondellBasell Industries | PP Copolymer | Softell |