Infino HM-1157
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FKgIvS_InfinoHM1157.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino HM-1157 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product, which contains a glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.10 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.10 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.10 | % | ISO 2577 |
| Traffic : 3.20mm | 0.10 | % | ISO 2577 |
| Ash Content | |||
| -- | 15 | % | ASTM D5630 |
| -- | 15 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3700 | MPa | ASTM D638 |
| -- | 3800 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 89.0 | MPa | ASTM D638 |
| Yield | 90.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 88.0 | MPa | ASTM D638 |
| Fracture | 90.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 3.0 | % | ASTM D638 |
| Fracture | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 4700 | MPa | ASTM D790 |
| -- 6 | 4800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 120 | MPa | ASTM D790 |
| -- 8 | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 49 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 49 | J/m | ASTM D256 |
| 23°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 91.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 91.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-1 | UL 94 | |
| 3.0 mm | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RV250LW 100 NAT 4861 | Radici Plastics | Nylon 66 | Radilon® |
| Hylon® N1045HL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| PEXTIN™ PBTM30-BK10 | Pier One Polymers, Inc. | PBT | PEXTIN™ |
| TechnoFiber PP LGF 50-10-01 H | TechnoCompound GmbH | PP, Unspecified | TechnoFiber |
| Hostacom TRC 333N G72862 | LyondellBasell Industries | PP Copolymer | Hostacom |