VITAMIDE® AW38BK6150
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FKg77f_VITAMIDE-AW38BK6150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® AW38BK6150 is a Polyamide 66 (Nylon 66) product filled with 40% carbon fiber. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 270 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 21000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 400 | MPa | ISO 178 |
| Break | 400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 30 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 265 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 260 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 1218, ASTM D2117 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 10 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® 663HS | Celanese Corporation | TPC-ET | Riteflex® |
| Starflam PX06106 | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| Latamid 66 B H-V0 | LATI S.p.A. | Nylon 66 | Latamid |
| Sylvin 6257-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polyethylene Bio TPSeal® 1100_03 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |