RELENE® C 31101
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FHpepy_RELENE-C-31101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Relene C 31101 is a black high density polyethylene compound for coating of metal pipes. It contains minimum 2% well dispersed, fine particle size carbon black in order to ensure excellent weathering resistance. Relene C 31101 offers excellent processability and adhesion characteristics. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.27 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (Compression Molded, F50) | 400 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 22.0 | MPa | ASTM D638 |
| Fracture, molding | 27.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 800 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 730 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.40 | ASTM D150 | |
| Dissipation Factor | 5.0E-4 | ASTM D150 |
| Additional Information |
|---|
| Oxidation Induction Time, ASTM D3895: >65 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| METALCAP PPC372B73 | Polyram Ram-On Industries | PP Copolymer | METALCAP |
| Kumho EP HAC 8240B | Korea Kumho Petrochemical Co., Ltd. | PC+ABS | Kumho EP |
| Indothene HD 50MA045 | Reliance Industries Limited | HDPE | Indothene HD |
| Karina PVC COMPOUND E-105911-35/1-BY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| 3M™ Dyneon™ PTFE Compound 1191 N | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |