OMIKRON BLV 802 NERO/E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TECNOPOL |
| Trademark: | OMIKRON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FGsXAI_OMIKRON-BLV-802-NERO-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OMIKRON BLV 802 NERO/E is an homopolymer polypropylene (high crystallinity) with 30% of glass fibre chemical bonded, for injection moulding, good processability. It is available in black version. Natural or coloured on demand. OMIKRON BLV 802 NERO/E is suitable for moulding of items requiring stiffness and dimensional stability . It is used in production of automotive components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 98.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 11 | kJ/m² | ISO 180 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging (150°C) | > 6.3 | day | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 153 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 136 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 220 - 250 | °C | |
| Middle Temperature | 220 - 250 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Pressure | 9.00 - 11.0 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 5.00 - 10.0 | MPa |
| Injection instructions |
|---|
| Post Pressure: 60 - 80 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P30B11 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| Sindustris PP HR2101D | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Telcar® TL-1934C | Teknor Apex Company | TPE | Telcar® |
| Moplen EP540V | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| NuSil MED1-4213 | NuSil Technology | Silicone | NuSil |