PROTEQ™ C24UST23Z
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FFpGQP_PROTEQ-C24UST23Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ C24UST23Z is a polypropylene copolymer containing 13% mineral filler which has been impact modified, heat and UV stabilised. This grade has been developed for applications such as automotive bumper bar and fascia components, requiring easy die filling, dimensional stability, weathering resistance and high low temperature toughness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 24 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 64 | ||
| Shore D, 15 sec | 57 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 17.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 250 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1150 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 28.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 170 | J/m | |
| 0°C, 3.20 mm | 460 | J/m | |
| 23°C, 3.20 mm | 630 | J/m | |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 93.0 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 53.0 | °C | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 195 to 215 | °C | |
| Middle Temperature | 205 to 225 | °C | |
| Front Temperature | 215 to 235 | °C | |
| Processing (Melt) Temp | 220 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G10 211 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Cellophane™ K116HB20 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Elastocon® STK60B | Elastocon TPE Technologies | TPE | Elastocon® |
| K-Flex 3070 | Technovinyl Polymers India Ltd. | TPE | K-Flex |
| Jiangsu Meilan XXMLF3-14 | Jiangsu Meilan Chemical Co., Ltd. | Fluorelastomer | Jiangsu Meilan |