TOTAL Polypropylene PPC 3666
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FFT8pg_TOTAL-Polypropylene-PPC-3666.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPC 3666 is a heterophasic copolymer with a Melt Flow Index of 1.5 g/10 min. This resin offers an outstanding processability in combination with good melt strength and excellent mechanical properties. Polypropylene PPC 3666 has been developed for the extrusion of corrugated cardboard. It offers an excellent performance as well in other applications, including sheet and film extrusion and thermoforming. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 77 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | > 50 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | > 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 92.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 60.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5755 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| SINOF P130T-04 | SINOF HI-TECH MATERIAL CO. LTD | PPS | SINOF |
| Tenopom® POM B3 HF NTLA010 PR306 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| TROGAMID® T T5004 | Evonik Industries AG | Nylon 6/3T | TROGAMID® T |
| Chiao Fu PA6 MC312G30 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |