LNP™ STAT-KON™ EX01696C compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FDrw6x_LNPSTATKONEX01696Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON EX01696C is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System. Also known as: LNP* STAT-KON* Compound PDX-E-01696 CCS Product reorder name: EX01696C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3700 | MPa | ASTM D638 |
| Tensile Strength (Break) | 94.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.6 | % | ASTM D638 |
| Flexural Modulus | 3630 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 480 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 - 1.0E+8 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 354 - 366 | °C | |
| Front Temperature | 366 - 377 | °C | |
| Processing (Melt) Temp | 360 - 366 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP6503 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| Converge® Polyol HMA-2 | Novomer, Inc. | PC | Converge® |
| Hanwha Total PP GB72 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina GRAY PVC COMPOUND 805-18/105-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Rotuba CAP CP801 (9% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |