Trexprene® A40CW
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FD0XdG_Trexprene-A40CW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A40CW is a UV, heat stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This pre-colored compound is intended primarily for applications needing good compression set properties, excellent aesthetics and UV characteristics. This material can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 to 0.940 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 38 to 44 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow 1(100% Strain) | 1.10 | MPa | ISO 37 |
| Tensile Stress - Across Flow 2(Yield) | 3.00 | MPa | ISO 37 |
| Tensile Elongation - Across Flow 3(Break) | 300 | % | ISO 37 |
| Tear Strength - Across Flow 4 | 12 | kN/m | ISO 34-1 |
| Compression Set | |||
| 70°C, 22 hr | 30 | % | ASTM D395B |
| 125°C, 70 hr | 20 | % | ASTM D395B |
| 70°C, 22 hr 5 | 30 | % | ISO 815 |
| 125°C, 70 hr 6 | 20 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ISO 188 | ||
| 135°C, 1000 hr | -25 to 10 | % | |
| 150°C, 168 hr | -20 to 10 | % | |
| Change in Tensile Strain at Break in Air | ISO 188 | ||
| 135°C, 1000 hr | -30 to 10 | % | |
| 150°C, 168 hr | -25 to 10 | % | |
| Change in Shore Hardness in Air | ISO 188 | ||
| Shore A, 135°C, 1000 hr | -5.0 to 5.0 | ||
| Shore A, 150°C, 168 hr | -3.0 to 3.0 | ||
| Change in Tensile Properties | ISO 188 | ||
| Stress at 100% Elongation in Air, 1000 hrs : 135°C | -20 to 20 | % | |
| Stress at 100% Elongation in Air, 168 hrs : 150°C | -20 to 20 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Ozone Resistance (40°C) 7 | 0 Rating | ISO 1431-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -56.0 | °C | ASTM D746 |
| Type B | -56.0 | °C | ISO 812 |
| Note Message | |
|---|---|
| 1 . | Type 1, 500 mm/min |
| 2 . | Type 1, 500 mm/min |
| 3 . | Type 1, 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type A |
| 6 . | Type A |
| 7 . | 100 pphm, Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MERICAN® 9180P | Huachang Polymer Co., Ltd. | Polyester Alloy | MERICAN® |
| tefabloc® TP SD 333 50A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| HiFill® PA6/6 GF33 SL5 | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Luranyl® HT 190 | ROMIRA GmbH | PPE+Nylon 66 | Luranyl® |
| EnviroPCABS 2090 HSL | West Michigan Compounding | PC+ABS | EnviroPCABS |