NORYL™ FE1630PW resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FCugZn_NORYLFE1630PWresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Noryl* FE1630PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30% Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid engineering applications. Noryl* FE1630PW has been certified for potable water applications up to 85C in Europe and North America in limited colours |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/10.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.10 - 0.30 | % | Internal method |
| Transverse flow : 3.20mm | 0.20 - 0.50 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 240 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9580 | MPa | ASTM D638 |
| -- | 9600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 134 | MPa | ASTM D638 |
| Fracture | 133 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 2.4 | % | ASTM D638 |
| Fracture | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 7760 | MPa | ASTM D790 |
| -- 5 | 8120 | MPa | ISO 178 |
| Flexural Stress | 192 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 65.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6 | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 7 | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C | 75 | J/m | ASTM D256 |
| 23°C | 85 | J/m | ASTM D256 |
| -30°C 8 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 9 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 470 | J/m | ASTM D4812 |
| 23°C | 510 | J/m | ASTM D4812 |
| -30°C 10 | 30 | kJ/m² | ISO 180/1U |
| 23°C 11 | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 100 mm span 12 | 150 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 145 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 13 | 145 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 165 | °C | ISO 306/A50 |
| -- | 154 | °C | ISO 306/B50 |
| -- | 158 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 sp=62mm |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0339C10L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Axiall PVC 18753 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Colorite Rigid PVC 2690 CLR | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| IPC PP 4833H-T | International Polymers Corporation | PP Homopolymer | IPC PP |
| Pibiflex® L6360 NAT | SO.F.TER. SPA | TPC-ET | Pibiflex® |