Order Products : sales@su-jiao.com
LNP™ THERMOCOMP™ OF008E compound
| Category: | PPS , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FCctVB_LNPTHERMOCOMPOF008Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP OF008E is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound OF-1008 EM Product reorder name: OF008E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture | 179 | MPa | ASTM D638 |
| Fracture | 160 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.7 | % | ASTM D638 |
| Fracture | 1.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 14300 | MPa | ASTM D790 |
| -- | 13400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 248 | MPa | ASTM D790 |
| -- | 190 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.66 | ASTM D3702 Modified | |
| With Self-Static | 0.87 | ASTM D3702 Modified | |
| Wear Factor - Washer | 240 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 1 | 6.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 590 | J/m | ASTM D4812 |
| 23°C 2 | 21 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 261 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 272 | °C | ISO 75-2/Af |
| CLTE - Flow (-40 to 40°C) | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.450 mm, Testing by SABIC) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vital-Line SHE9505G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| NEXUS PE HDPE-0350 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| Daelim Po1y® LL-32HF | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| Lifoflex® UV FLAM 60700 | Müller Kunststoffe GmbH | TPE | Lifoflex® |
| ZEONOR® 1410R | Zeon Corporation | COP | ZEONOR® |