Description Low Thermal Conductivity, Chemical Resistance, High Heat Resistance Application Electrical or Electronic Parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (290°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 118 | MPa | ASTM D638 |
| Flexural Modulus 2(3.20 mm) | 10800 | MPa | ASTM D790 |
| Flexural Strength 3(Yield, 3.20 mm) | 177 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm 4 | 260 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm 5 | 220 | °C | |
| Thermal Conductivity | 0.40 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 270 to 320 | °C | |
| Front Temperature | 275 to 320 | °C | |
| Nozzle Temperature | 315 | °C | |
| Processing (Melt) Temp | 315 | °C | |
| Mold Temperature | 80.0 to 130 | °C | |
| Back Pressure | 0.981 to 2.94 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 4.6kg |
| 5 . | 18.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P598 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| ALCOM® PWL 10/1 WT41-913LB | ALBIS PLASTIC GmbH | PC | ALCOM® PWL |
| DIC.PPS FZ-1130 | DIC Corporation | PPS | DIC.PPS |
| HAIPLEN EP150 C4 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| LNP™ LUBRICOMP™ RX93237 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |