QAMAR FD21HS
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SPDC Ltd. |
| Trademark: | QAMAR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FAkQ7i_QAMAR-FD21HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
QAMAR FD21HS is a linear low density polyethylene material,. This product is available in North America. The processing method is: blown film or cast film. The main features of QAMAR FD21HS are:
The typical application fields of QAMAR FD21HS are: movies |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 54 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | JIS K6760 | ||
| Yield | 12.0 | MPa | JIS K6760 |
| Fracture | 26.0 | MPa | JIS K6760 |
| Tensile Strain (Break) | 900 | % | JIS K6760 |
| Apparent Bending Modulus | 260 | MPa | ASTM D747 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Modulus | ISO IR 1184 | ||
| MD : 30 µm | 190 | MPa | ISO IR 1184 |
| TD : 30 µm | 210 | MPa | ISO IR 1184 |
| Tensile Stress | JIS Z1702 | ||
| MD : Break, 30 µm | 40.0 | MPa | JIS Z1702 |
| TD : Break, 30 µm | 35.0 | MPa | JIS Z1702 |
| Tensile Elongation | JIS Z1702 | ||
| MD : Break, 30 µm | 600 | % | JIS Z1702 |
| TD : Break, 30 µm | 900 | % | JIS Z1702 |
| Dart Drop Impact (30 µm) | 110 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm | 30 | g | ASTM D1922 |
| TD : 30 µm | 140 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 190 | °C | |
| Melt Temperature (Aim) | 180 | °C |
| Extrusion instructions |
|---|
| Blow up Ratio: 2 to 4Screw Type: LLDPE screwDie Lip Gap: 2.0 to 3.0 mmAir Ring: Single or Dual Slit (Wide die) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ZYLAR® 650 | INEOS Styrolution Group GmbH | MMBS | ZYLAR® |
| Epoxies, Ect. 10-3020 NS | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| HiFill® PA6 IM L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Karina RED PVC COMP. -E 850-42/231-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MARPOL® EVA 1707 | Marco Polo International, Inc. | EVA | MARPOL® EVA |