Baytec® SPR-092A Black
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F9n95H_Baytec-SPR-092A-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Baytec SPR-092A Black is a two-component, 100%-solids thick film coating spray system with a Shore A hardness of 92. The isocyanate component is a modified diphenylmethane diisocyanate (MDI) prepolymer, and the B component is a polyether polyol amine blend. The system has added UV stabilizers and is used in industrial applications to improve the corrosion, weather, and abrasion resistance of various surfaces. The system is pigmented black. Typical applications include wastewater infrastructure, pipes, secondary containment, foams, and other industrial surfaces. As with any product, use of the Baytec SPR-092A Black system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Water absorption rate- 30 days | 1.5 | % | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength, Split | 19.3 - 22.8 | kN/m | ASTM D1938 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 150 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 15.2 - 15.9 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 490 - 580 | % | ASTM D412 |
| Tear Strength 1 | 59.5 - 71.8 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by capacity: 100 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Part A Type: Isocyanate Appearance: Yellowish liquid Specific Gravity @ 25°C: 1.09 Viscosity @25°C: 2500 mPa-s Flash Point PMCC: 216 °C Part B Type: Polyol Appearance: Black liquid Specific Gravity @ 25°C: 1.04 Viscosity @25°C: 1704 mPa-s Flash Point PMCC: 179 °C Molding Parameters Material Temperature: 60 to 71 °C Gel Time: 12 to 15 sec Tack-Free Time: 1 min Handling Time: 30 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® HPN 9362 | BASF Corporation | Nylon 6 | Ultramid® |
| INNOPOL® PP CS 2-9522 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| LONGLITE® LCP LCP-300 B3G | CCP Group | LCP | LONGLITE® LCP |
| POLYfill PPC T1010 | Polykemi AB | PP Copolymer | POLYfill |
| Durethan® BKV 30 H2.0 901510 | LANXESS GmbH | Nylon 6 | Durethan® |