SANREX SAN-T
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | SANREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F9LnbM_SANREX-SAN-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SANREX SAN-T is a Styrene Acrylonitrile (SAN) product. It can be processed by injection molding and is available in Asia Pacific or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.50 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| M-Scale | 83 | ASTM D785 | |
| M-Scale | 82 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 90.2 | MPa | ASTM D638 |
| Yield | 79.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3820 | MPa | ASTM D790 |
| -- | 3210 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 128 | MPa | ASTM D790 |
| -- | 107 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.7 | kJ/m² | ISO 179 |
| Notched Izod Impact | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 96.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 87.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (ALL) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 190 to 260 | °C | |
| Middle Temperature | 190 to 260 | °C | |
| Front Temperature | 190 to 260 | °C | |
| Mold Temperature | 20.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Capilene® HT 75 A | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| CERTENE™ LDF-224C | Muehlstein | LDPE | CERTENE™ |
| LEXAN™ FXM121R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| LNP™ STAT-KON™ REF42I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| LUVOCOM® 1-RG 3 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |