FARBOSET® 2461
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Cosmic Plastics, Inc. |
| Trademark: | FARBOSET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F8q2VH_FARBOSET-2461.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cosmic FARBOSET 2461 Black is a mineral-filled epoxy molding compound featuring fast cure rates, superb moldability, excellent thermal shock and moisture resistance. This compound was especially formulated to achieve a high glass transition temperature for optimum reliability performance in very thin sections. It is designed to encapsulate a wide range of devices including capacitors, resistors, and inductor coils. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.88 | g/cm³ | |
| -- 1 | 2.08 | g/cm³ | |
| Apparent Density 2 | 0.90 | g/cm³ | |
| Spiral Flow | 76.0 | cm | |
| Molding Shrinkage - Flow | 0.40 | % |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | 56.5 | MPa | |
| Flexural Modulus | 13400 | MPa | |
| Flexural Strength | 85.5 | MPa | |
| Compressive Strength | 236 | MPa |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | 163 | °C | |
| CLTE - Flow | |||
| -- 3 | 2.7E-5 | cm/cm/°C | |
| -- 4 | 6.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.96 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.5E+15 | ohms | |
| Volume Resistivity | 2.2E+15 | ohms·cm | |
| Dielectric Strength (6.35 mm) | 15 | kV/mm | |
| Dielectric Constant (1 kHz) | 5.12 | ||
| Dissipation Factor (1 kHz) | 0.012 | ||
| Arc Resistance | 194 | sec |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Tested by Cosmic Plastics) | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life 5 | |||
| 4°C | 52 | wk | |
| 25°C | 1.0 | wk | |
| 35°C | 0.29 | wk | |
| Post Cure Time (150°C) | 4.0 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time | |||
| 150°C 6 | 8.6E-3 | hr | |
| 150°C | 0.017 to 0.033 | hr |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 145 to 180 | °C | |
| Injection Pressure | 1.38 to 6.89 | MPa |
| Note Message | |
|---|---|
| 1 . | Molded |
| 2 . | Powder |
| 3 . | Alpha 1 |
| 4 . | Alpha 2 |
| 5 . | Defined as not more than 40% loss of spiral flow based on original values. |
| 6 . | Hot Plate Cure Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDM 520 | Marco Polo International, Inc. | HDPE | MARPOL® |
| Sinvicomp SGH8000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Hanwha Total PP TH52 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Kemcor LD 8153 | Qenos Pty Ltd | LDPE | Kemcor |
| Hy-Vin® GD2815A | INEOS Compounds | PVC, Flexible | Hy-Vin® |