TIPPLEN® K 850
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F7G8cl_TIPPLEN-K-850.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPPLEN K 850 is a bimodal, high molecular weight impact copolymer polypropylene for extrusion. TIPPLEN K 850 offers excellent heat and detergent resistance. The product shows very high stiffness, high impact strength and excellent processability. Applications TIPPLEN K 850 is well suited for blow moulded appliance components, wheels, under-the-hood automotive parts, toolboxes, suitcases and large containers. TIPPLEN K 850 is also applicable for extrusion of pipes, corrugated pipes, and fittings, tough sheet for industrial applications and thermoforming trays for storage in refrigerator. TIPPLEN K 850 is suitable for food contact. The product complies with Food Contact Regulations. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.23 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1800 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Injection Molded) | 36.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, Injection Molded) | 10 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 1850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -20°C, Injection Molded | 5.0 | kJ/m² | |
| 23°C, Injection Molded | 46 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 116 | °C | ISO 75-2/B |
| Oxidation Induction Time (200°C) | 120 | min | EN 728 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 195 to 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 128 HI UV | RTP Company | PP Copolymer | RTP |
| SABIC® HDPE B5260LS | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Network Polymers SBS 1000 | Network Polymers, Inc. | SBS | Network Polymers SBS |
| Chemical Resources PA612158S | Chemical Resources, Inc. | Nylon 612 | Chemical Resources |
| LNP™ LUBRICOMP™ PFL38S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |