Order Products : sales@su-jiao.com
Akulon® K225-KV
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F6QSaP_Akulon-K225-KV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® K225-KV is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific, Europe, or North America. Important attributes of Akulon® K225-KV are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.21 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 1.0 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4200 | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 70.0 | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.0 | 30 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 4.0 | > 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.0 | 5.0 | kJ/m² | |
| 23°C | 4.0 | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 40 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.30 | 8.00 | ||
| 1 MHz | 3.20 | 3.60 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 9.0E-3 | 0.13 | ||
| 1 MHz | 0.020 | 0.080 | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.380 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.380 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.380 mm | 930 | -- | °C | |
| 3.00 mm | 850 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 225 to 230 | °C | |
| Middle Temperature | 230 to 235 | °C | |
| Front Temperature | 230 to 240 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 245 to 255 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOCOMP® PBT TS7 | EPIC Polymers | PBT | TRIBOCOMP® |
| FERREX® GPP20CF21HB-NA | Ferro Corporation | PP, Unspecified | FERREX® |
| Hostacom TRC 1193N | LyondellBasell Industries | TPO (POE) | Hostacom |
| OTECH ALLOY OW138 - Cord Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| ULTEM™ 4001 resin | SABIC Innovative Plastics | PEI | ULTEM™ |