Sasol Polymers PP CPV340

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	Sasol Polymers
Trademark:	Sasol Polymers PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	F5o24U_Sasol-Polymers-PP-CPV340.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Features

High flow

Narrow molecular weight distribution

Suitable for injection moulding of thin walled articles, requiring medium impact and stiffness

Contains a nucleating agent which ensures rapid crystallisation, resulting in an improved impact to stiffness balance as well as shorter cooling times

Applications
Injection moulding

Stadium seating

Household and domestic articles

Caps and closures

Boxes and containers

Indoor furniture

Cosmetic containers

General Information
Additive	Nucleating agent Unspecified additive
Features	Nucleated Rigid, good Impact copolymer High liquidity Compliance of Food Exposure Narrow molecular weight distribution Medium impact resistance
Uses	Thin wall parts Shield Furniture Household goods Container Shell
Agency Ratings	EC 1935/2004 FDA 21 CFR 177.1520(a)(3)(i)(c)(1) FDA 21 CFR 177.1520(c) 3.1a
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	16	g/10 min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction	1.3	%	ISO 294-4
Flow direction	1.3	%	ISO 294-4

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	60.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1400	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	28.0	MPa	ISO 527-2/1A/50
Tensile Strain			ISO 527-2/1A/50
Yield	6.5	%	ISO 527-2/1A/50
Fracture	> 50	%	ISO 527-2/1A/50
Flexural Modulus	1350	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-20°C	2.8	kJ/m²	ISO 179/1eA
0°C	3.5	kJ/m²	ISO 179/1eA
23°C	6.0	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	88.0	°C	ISO 75-2/B
1.8 MPa, not annealed	51.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	151	°C	ISO 306/A120
--	67.0	°C	ISO 306/B120
Melting Temperature	163	°C	ISO 11357-3

Injection	Nominal Value	Unit
Hopper Temperature	40.0 - 60.0	°C
Rear Temperature	180 - 260	°C
Middle Temperature	220 - 280	°C
Front Temperature	240 - 280	°C
Nozzle Temperature	220 - 280	°C
Processing (Melt) Temp	220 - 280	°C
Mold Temperature	20.0 - 60.0	°C

Injection instructions
Zone 4: 240 to 280°C

Resin Grade	Manufacturer	Category	Trademark
Fainplast PVC RH 612	Fainplast Compounds S.r.l	PVC, Rigid	Fainplast PVC
Hanwha Total PP TB52U	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, High Crystal	Hanwha Total PP
ICORENE® 1761 V2 Black 9004	ICO Polymers EMEA, A Division of A. Schulman	mMDPE	ICORENE®
Karina IVORY PVC COMPOUND BTR-85/200-D-IS-BS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Sylvin 9302-70 FUV WHITE 1264	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin