LNP™ LUBRICOMP™ KFP032 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F5YUdw_LNP-LUBRICOMP-KFP032-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* KFP032 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KFL-4532 Product reorder name: KFP032 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 1.52 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5030 | MPa | ASTM D638 |
| -- | 4810 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 67.0 | MPa | ASTM D638 |
| Break | 64.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.6 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 4180 | MPa | ASTM D790 |
| -- 5 | 4130 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 95.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 100 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 94.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 39 | J/m | ASTM D256 |
| 23°C 8 | 3.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D4812 |
| 23°C 9 | 24 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 5.62 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 162 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 161 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 159 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 148 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF2705 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Unichem 4060A | Colorite Polymers | PVC, Unspecified | Unichem |
| Hostacom EKC485N | LyondellBasell Industries | PP Copolymer | Hostacom |
| Lucent PP GPP-220 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| Therma-Tech™ TT9200-5010 EC Anthracite | PolyOne Corporation | PPS | Therma-Tech™ |