LNP™ STAT-KON™ DE0069F compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F4yBxa_LNP-STAT-KON-DE0069F-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DE0069F is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Superior Molding. Also known as: LNP* STAT-KON* Compound DC-1006 FR SM Product reorder name: DE0069F |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.010 to 0.030 | % | |
| Across Flow : 24 hr | 0.10 to 0.40 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17300 | MPa | ASTM D638 |
| -- | 16700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 146 | MPa | ASTM D638 |
| Yield | 1.37 | MPa | ISO 527-2/5 |
| Break 3 | 146 | MPa | ASTM D638 |
| Break | 137 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.7 | % | ASTM D638 |
| Yield | 1.3 | % | ISO 527-2/5 |
| Break 5 | 1.7 | % | ASTM D638 |
| Break | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 14600 | MPa | ASTM D790 |
| -- 7 | 14600 | MPa | ISO 178 |
| Flexural Strength 8 | ASTM D790 | ||
| Yield, 50.0 mm Span | 210 | MPa | |
| Break, 50.0 mm Span | 212 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 52 | J/m | ASTM D256 |
| 23°C 9 | 5.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 460 | J/m | ASTM D4812 |
| 23°C 10 | 25 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 10.0 | J | ASTM D3763 |
| -- | 2.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 146 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 148 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 142 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 143 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.0E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.0E-6 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 to 4.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cheng Yu NG1400S | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| Chemical Resources PP 1200NW1 | Chemical Resources, Inc. | PP Homopolymer | Chemical Resources |
| Ferro PP LPP25BC64NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Hylon® N2013L | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| tivilon® DP2272/85AF | API SpA | TPV | tivilon® |