RTP 1305.3 P-1
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F4dEqg_RTP-1305-3-P-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13800 | MPa | ASTM D638 |
| Tensile Strength | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.7 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Flexural Strength | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 450 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 2mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 302 - 343 | °C | |
| Middle Temperature | 302 - 343 | °C | |
| Front Temperature | 302 - 343 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 103 - 138 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPC PVC SM61E | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Chemiton CSF0NA 90 | Franplast S.r.l. | SEBS | Chemiton |
| Kazan LDPE 16813-070 OKP 22 111 4102 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| LNP™ LUBRICOMP™ WCL36 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |
| Machine Cast MC-90 A/B | BJB Enterprises, Inc. | TSU | Machine Cast |