ETILINAS LL0207MA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | POLYETHYLENE MALAYSIA SDN BHD |
| Trademark: | ETILINAS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F4NLDX_ETILINAS-LL0207MA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ETILINAS LL0207MA is a linear low density polyethylene suitable for a variety of film applications. Characteristics include: high strength, no slip agent, and medium level of antiblocking agent. Applications include: sack films, and other heavy duty films. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield | 11.0 | MPa | ISO 527-3 |
| TD : Yield | 12.0 | MPa | ISO 527-3 |
| MD : 38 µm | 42.0 | MPa | ISO 527-3 |
| TD : 38 µm | 33.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 38 µm | 630 | % | ISO 527-3 |
| TD : Fracture, 38 µm | 830 | % | ISO 527-3 |
| Dart Drop Impact (38 µm) | 180 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 38 µm | 2.5 | N | ISO 6383-2 |
| TD : 38 µm | 6.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306 |
| Melting Temperature (DSC) | 122 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm) | 52 | ASTM D2457 | |
| Haze (38.0 µm) | 11 | % | ASTM D1003 |
| Additional Information |
|---|
| Density, ISO 1872/1, Annealed: 920 kg/m³Melting Point, ISO 3146, Method C: 122°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 4022 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Fluoroplex MAXSEAT MRNA - GMF | UNIFLON | PTFE | Fluoroplex |
| Hifax EYC 335P | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| CABELEC® CC6135 | Cabot Corporation | PS (GPPS) | CABELEC® |
| CYCOLOY™ CY6414 resin | SABIC Innovative Plastics Europe | PC | CYCOLOY™ |