LIHAN® A707MO
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F3cgBx_LIHAN-A707MO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LIHAN® A707MO is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 to 0.50 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.60 to 1.0 | -- | % | ISO 62 |
| Water Content | 5.0 to 6.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 115 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Break) | 185 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 8700 | 6000 | MPa | ISO 178 |
| Flexural Stress | 240 | 190 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 12 | 17 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | DSC |
| CLTE - Flow | 1.5E-5 to 2.0E-5 | 6.0E-5 to 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | ASTM D257 |
| Dielectric Strength | 20 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.59 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 265 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8202-82FU White 1226 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Trademark PE LD0720C | Trademark Plastics Corporation | LDPE | Trademark PE |
| Yuyao PA 05ZR16 | Yuyao Tenglong Plastics Co., Ltd. | Nylon 66/6 | Yuyao PA |
| Chemical Resources HD2955 | Chemical Resources, Inc. | HDPE | Chemical Resources |
| LNP™ LUBRICOMP™ RL004S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |