Maxxam™ PP5940 B131 C
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F3Bx6V_Maxxam-PP5940-B131-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fiber and mica reinforced PP compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 67.0 | MPa | ISO 527 |
| Tensile Elongation (Break, 23°C) | 2.5 | % | ISO 527 |
| Flexural Modulus (23°C) | 6700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 5.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 138 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ WCD895 resin | SABIC Innovative Plastics Asia Pacific | PPE+TPE | NORYL™ |
| ALCUDIA® HDPE M5309 | REPSOL | HDPE | ALCUDIA® HDPE |
| ARMAMID® PA SVMN 35-1 | Poly Plastic | Nylon 6 | ARMAMID® |
| Indothene HD 46GP003 | Reliance Industries Limited | HDPE | Indothene HD |
| Lucene™ LC175 | LG Chem Ltd. | TPO (POE) | Lucene™ |