Lupol® GP1007FE
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F22QUi_Lupol-GP1007FE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, Flame Retardant Application Electrical & Electronic, Automotive Parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.6 to 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 200 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 981 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 29.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | > 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, 3.20 mm) | 110 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-2 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Cylinder Zone 1 Temp. | 190 to 210 | °C | |
| Cylinder Zone 2 Temp. | 200 to 230 | °C | |
| Cylinder Zone 3 Temp. | 220 to 240 | °C | |
| Cylinder Zone 4 Temp. | 220 to 240 | °C | |
| Melt Temperature | 230 to 245 | °C | |
| Die Temperature | 220 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | 4.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EPO-TEK® B9021-15 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Karina BLUE COLOR CONCENTRATE 06/830-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina ORANGE COLOR CONCENTRATE 32/1-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MACOMASS TPE MM-TPE V 3140 | MACOMASS Verkaufs AG | TPE | MACOMASS TPE |
| POLLITE 1002G30 | POLYROCKS CHEMICAL CO., LTD | PC | POLLITE |