3M™ Dyneon™ TFM™ Modified PTFE TFR 1502 A

Category:	PTFE , Polytetrafluoroethylene
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ TFM™ Modified PTFE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	F1mGAo_3M-Dyneon-TFM-Modified-PTFE-TFR-1502-A.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Modified PTFE for ram extrusion

Features

Tailor made for ram extrusion

Excellent free-flowing characteristics with easy feeding

Reduced deformation under load (cold flow)

Good mouldability

Low porosity and reduced permeability

Excellent product smoothness

Improved weldability

Typical Applications

Ram extrusion of rods and profiles with wall thickness preferably greater than 12mm

Ram extrusion of tubes with wall thickness preferably greater than 4 mm

Semi-finished articles

General Information
Features	Good Flow Good Moldability Weldable
Uses	Profiles Rods Tubing
Processing Method	Ram Extrusion

Physical	Nominal Value	Unit	Test Method
Density	2.16	g/cm³	ISO 12086
Apparent Density	0.80	g/cm³	ISO 60
Molding Shrinkage ¹(23.0 mm)	11	%	Internal Method
Average Particle Size	800	µm	ISO 13320

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	53		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Deformation Under Load			ASTM D621
23°C, 15 MPa ²	6.00	%
23°C, 15 MPa ³	14.0	%

Films	Nominal Value	Unit	Test Method
Tensile Strength (500 µm)	35.0	MPa	ISO 527-3
Tensile Elongation (Break, 500 µm)	500	%	ISO 527-3

Thermal	Nominal Value	Unit	Test Method
Thermal Conductivity	0.22	W/m/K	DIN 52612

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+17	ohms	IEC 60093
Volume Resistivity	1.0E+18	ohms·cm	IEC 60093

Note Message
1 .	ram extruded rod
2 .	remaining
3 .	100 h

Resin Grade	Manufacturer	Category	Trademark
SUMILITE® PVC VSS-F120	Sumitomo Bakelite Co., Ltd.	PVC, Unspecified	SUMILITE® PVC
Vikalloy P51	Viking Polymers, LLC	PMMA+PVC	Vikalloy
ACCUTECH™ HP0339G10CL	ACLO Compounders Inc.	PP Homopolymer	ACCUTECH™
EvoSource™ ABS 4535 90/05	MBA Polymers	ABS	EvoSource™
POTICON OB30	Otsuka Chemical Co., Ltd.	PBT	POTICON