VALOX™ K3501 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F1PbYX_VALOXK3501resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled PBT, Hydrollytically Stable, Heat Stabilized, Impact Modified. A hydrollytically stable grade designed for improved performance under heat/humidity environments. Targeted at automotive underhood applications requiring USCAR-2 Class III humidity/heat performance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 26.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.34 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 50.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 25.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield 4 | 3.5 | % | ASTM D638 |
| Yield | 3.5 | % | ISO 527-2/50 |
| Fracture 5 | 50 | % | ASTM D638 |
| Fracture | 40 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2100 | MPa | ASTM D790 |
| -- 7 | 2000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 70.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C | 75 | J/m | ASTM D256 |
| 0°C | 80 | J/m | ASTM D256 |
| 23°C | 90 | J/m | ASTM D256 |
| 23°C 9 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (-30°C) | No Break | ASTM D4812, ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 45.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 45.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 165 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 9.7E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 76.7 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PP 1381 | Premix Oy | PP, Unspecified | PRE-ELEC® |
| Tecolen® CP30 NL XC30 | Eurotec Engineering Plastics | PP Copolymer | Tecolen® |
| Sylvin 6175-74 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NYLOPAK™ 570P | The Dow Chemical Company | Nylon, Unspecified | NYLOPAK™ |
| NYCOA Polyamide 2046 | Nycoa (Nylon Corporation of America) | Nylon 6/69 | NYCOA Polyamide |